Custom 465® Stainless Steel Bar - ASTM F899
Custom 465® is a premium melted, martensitic, age-hardenable stainless steel alloy. This material was designed with improved tensile strength, fracture toughness and improved fabricability and excellent resistance to stress corrosion cracking. It has been used in the medical industry, oil and gas drilling, aerospace components, marine equipment, firearms and hand tools.
Standard Inventory Specifications
- UNS S46500
- ASTM F 899
Common Trade Names
- Custom 465 (® Carpenter Technology Corporation)
- CarTech® Custom 465® Stainless
Common Applications of Custom 465 ® Stainless Steel
- Surgical instruments for orthopedic, spinal, and dental markets
- Drill Bits
- Drivers
- Distractors
- Shafts
- Aerospace
- Oil and gas
- Sports equipment
Inventory Size Range
- Bar : 0.125" - 3.000"
Our medical grade stainess steel round bar is domestic melted and manufactured. Incoming material includes screw machine quality Custom 465® with tolerances of +/- .0005". All sizes below .75" round are stocked to a bar tolerance of +/- .0005".
Please contact us for more details.
United Performance Metals is Approved ISO 13485 : 2003. The technical data provided is for information only and not for design purposes. It is not warranted or guaranteed.
Chemical Composition of Custom 465®
|
C |
P |
Si |
Ni |
Ti |
|
|---|---|---|---|---|---|
|
MIN |
__ |
__ |
__ |
10.75 |
1.50 |
|
MAX |
0.02 |
0.015 |
0.25 |
11.25 |
2.50 |
|
Mn |
S |
Cr |
Mo |
Fe |
|
|---|---|---|---|---|---|
|
MIN |
__ |
__ |
11.00 |
0.75 |
|
|
MAX |
0.25 |
0.010 |
12.50 |
1.25 |
Bal. |
Custom 465® Physical Properties
|
Density Condition |
g/cm³ |
|---|---|
|
Annealed/CT |
7.81 |
|
H900 |
7.82 |
|
H950 |
7.83 |
|
H1000 |
7.84 |
|
H1050 |
7.86 |
|
H1100 |
7.86 |
Custom 465® Mechanical Properties
|
Condition |
H950 |
|
Yield Strength, MPa (ksi) |
1648 (239) |
|
Ultimate Tensile Strength MPa (ksi) |
1751 (254) |
|
Elongation |
14% |
|
Reduction in Area |
63% |
|
Fracture Toughness |
98 (89) |
|
Charpy V-Notch Energy, J (ft-lb) |
27 (20) |